Ultrasonic Flaw Detector
-
Ultrasonic Thickness Gauge
-
Coating Thickness Gauge
-
Portable Hardness Tester
-
X-Ray Flaw Detector
-
X-ray Pipeline Crawlers
-
Holiday Detector
-
Magnetic Particle Testing
-
Eddy Current Testing Equipment
-
Penetrant Testing
-
Shore Durometer
-
Brinell Hardness Tester
-
Rockwell Hardness Tester
-
Micro Vickers Hardness Tester
-
Material Hardness Tester
-
Vibration Meter
-
Surface Roughness Tester
-
Profile Projector
-
Gloss Meters
-
Concrete Test Hammer
-
Laser Infrared Thermometer
-
bobAstm E114-15 Inch Type 1018 Calibration Test Block Carbon Steel Mini Iiw 2
-
WilliamAstm E114-15 Inch Type 1018 Calibration Test Block Carbon Steel Mini Iiw 2
-
tomAstm E114-15 Inch Type 1018 Calibration Test Block Carbon Steel Mini Iiw 2
-
LeoAstm E114-15 Inch Type 1018 Calibration Test Block Carbon Steel Mini Iiw 2
Cross Hatch Cutter ISO 2409-1992, GB/T9286-98, BS 3900 E6 And ASTM D3359 Standards

Contact me for free samples and coupons.
WhatsApp:0086 18588475571
Wechat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xHighlight | digital thickness gauge,coating thickness meter |
---|
Cross Hatch Cutter
Product Introduction:
2202 Cross Hatch Cutter is designed and manufactured according to ISO 2409-1992, GB/T9286-98, BS 3900 E6 and ASTM D3359 standards.
Introduction:
2202 Cross Hatch Cutter is designed and manufactured according to ISO 2409-1992, GB/T9286-98, BS 3900 E6 and ASTM D3359 standards.
Technical Specification:
Cutting Head No. | Gap(mm) | Blades | Cutters Edges | Coating Thickness(µm) |
2202/1 | 1 | 6 | 8 | 0~60 |
2202/2 | 1 | 11 | 8 | 0~60 |
2202/3 | 1.5 | 6 | 8 | 0~60 |
2202/4 | 2 | 6 | 8 | 61~120 |
2202/6 | 3 | 6 | 8 | 121~250 |
Order Information :
Standard Kit | Contain |
2202/1C | Cross Hatch Cutter + Carry Case + Hexagonal Screwdriver + Brush + Magnifier + Tape |
2202/2C | |
2202/3C | |
2202/4C | |
2202/6C | |
Simple Kit | Contain |
2202/1S | Cross Hatch Cutter + Paper Box + Hexagonal Screwdriver |
2202/2S | |
2202/3S | |
2202/4S | |
2202/6S |
Evaluation Criteria of Coating Adhesion Test:
Evaluation according to scale below:
Description | Performance | Class(ASTM) | Class(ISO) |
The edges of the cuts are completely smooth; none of the squares of the lattice is detached | 5B | 0 | |
Detachment of small flakes of the coating at the intersections of cuts. A cross-cut area not significantly greater than 5% is affected | ![]() |
4B | 1 |
The coating has flaked along the edges and/or at the intersections of the cuts. A cut area significantly greater than 5%, but not significantly greater than 15% is affected | ![]() |
3B | 2 |
The coating has flaked along the edges of the cuts partly or wholly in large ribbons, and or it has flaked partly or wholly on different parts of the squares. A cross cut area significant greater than 35% is affected | ![]() |
2B | 3 |
The coating has flaked along the edges of the cuts in large ribbons and/or same square have detached parity or wholly. A cross-cut area significantly greater than 35%, but not significantly greater than 60% is affected | ![]() |
1B | 4 |
Any degree of flaking that cannot even be classified | 0B | 5 |